SIHARD 2080 Steel
Designation by Standards
Brand Name | Ravne | Mat. No. | DIN | EN | AISI/SAE |
SIHARD 2080 | OCR12 | 1.2080 | X210Cr12 | X210Cr12 | D3 |
Chemical Composition (in weight %)
C | Si | Mn | Cr | Mo | Ni | V | W | Others |
2.05 | 0.25 | 0.30 | 11.50 | - | - | - | - | - |
Description
D3 is an oil hardening, high carbon/chromium type tool steel with very high wear resistance. It hardens with a very slight change in size. The alloy possesses very high compressive strength and is deep hardening.
Applications
Cutting tools, stamping, woodworking, drawing, deep drawing and pressing tools, cold working rolls, measuring tools.
Physical properties (average values) at ambient temperature
Modulus of elasticity [103 x N/mm2]: 210 Density [g/cm3]: 7.67
Thermal conductivity [W/m.K]: 20.0
Electric resistivity [Ohm mm2/m]: 0.65 Specific heat capacity[J/g.K]: 0.46
Coefficient of Linear Thermal Expansion 10-6 oC-1
20-100oC | 20-200oC | 20-300oC | 20-400oC | 20-500oC | 20-600oC | 20-700oC |
11.7 | 12.0 | 12.4 | 12.9 | 13.3 | 13.6 | 14.0 |
Continuous Cooling Transformation (CCT) Diagram
ime-Temperature Transformation (TTT) Diagram
Soft Annealing
Heat to 800-840oC, cool slowly. This will produce a maximum Brinell hardness of 250. To secure uniform softness.
Stress Relieving
Stress relieving to remove machining stresses should be carried out by heating to 650oC, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening
Harden from a temperature of 940-980oC followed by oil quenching or warm bath approx. 400oC. Hardness after quenching is 64-66 HRC.
For small parts up to thickness 30 mm. Harden from a temperature of 960-100oC followed by air, comompressed air quenching. Hardness after quenching is 63-65 HRC.
Tempering
Tempering temperature: 150-400oC.
Tempering Temperature (oC) vs. Hardness (HRC)
100oC | 200oC | 300oC | 400oC | 500oC | 600oC |
64 | 62 | 60 | 57 | 53 | 42 |
Tempering Diagram
Forging
Hot forming temperature: 1050-850oC.
Machinability
The machinability rating of D3 is roughly 25 % that of free machining carbon steel 1018. Due to its abrasion resistant nature, machining in the hardened condition should be limited to finish grinding.
Forms manufactured: Please see the Dimensional Sales Program.
Disclaimer
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for material described herein are made solely for the purpose of illustration to enable the reader to make his own evaluation and are not intended as warranties, either express or implied, of fitness for these or other purposes. There is no representation that the recipient of this literature will receive updated editions as the become available.
Unless otherwise specified, registered trademarks are property of SIJ Metal Ravne company. Copyright 2016 by SIJ Metal Ravne d.o.o. All rights reserved. Contact our Sales Office for more information.