M2 High Speed Steel (M2) is a tungsten-molybdenum high speed steel with a well balanced composition suitable for a wide variety of applications. World wide, the M2 type is by far the most popular high speed steel having replaced T1 high speed in most applications because of its superior properties and relative economy.
Twist drills, taps, milling cutters, reamers, broaches, saws, and knives.
| PRECISION ALLOY2 |
| PRECISION ALLOY1 |
| HOT WORK TOOL STEEL2 |
| HOT WORK TOOL STEEL1 |
| COLD WORK TOOL STEEL2 |
| T1 1.3355 SKH2 |
| M42 |
| M2 1.3343 SKH9 |
COMPOSITION
| C | Mn | Si | Cr | W | Mo | V |
| 0.85 | 0.28 | 0.30 | 4.15 | 6.15 | 5.00 | 1.85 |
RELATIVE PROPERTIES
Coefficient of Thermal Expansion(65-66 HRC) | |||
Temperature︒F | in/in︒F×10-6 | Temperature︒C | mm/mm︒C×10-6 |
70-200 | 5.69 | 21-93 | 10.23 |
70-400 | 6.09 | 21-204 | 10.95 |
70-600 | 6.42 | 21-316 | 11.55 |
70-800 | 6.67 | 21-427 | 12 |
70-1000 | 6.97 | 21-358 | 12.54 |
PHYSICAL PROPERTIES
· Density: 0.294 lb/in3 (8138 kg/m3)
· Specific Gravity: 8.14
· Modulus of Elasticity: 30 x 106 psi (207GPa)
· Machinability: 50-60% of a 1% carbon steel
HEAT TREATING INSTRUCTIONS
HARDENING
CRITICAL TEMPERATURE： | |
Ac1: 1530°F(832℃） | Ac3: 1610°F(877℃） |
AR1: 1430°F(777℃） | AR3: 1380°F(749℃） |
Preheating: To minimize distortion and stresses in large or complex tools use a double preheat. Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1100°F (593°C) equalize, then heat to 1450-1550°F (788-843°C). For normal tools, use only the second temperature range as a single preheating treatment.
Austenitizing (High Heat): Heat rapidly from the preheat.
For Cutting Tools:
Furnace: 2200-2250°F (1204-1232°C)
Salt: 2175-2225°F (1191-1218°C)
To maximize toughness, use the lowest temperature.
To maximize hot hardness, use the highest temperature.
For punches, dies, and tools that require maximum
toughness without hot hardness:
Furnace: 2075-2175°F (1175-1191°C)
Salt: 2050-2150°F (1121-1177°C)
Quenching: Pressurized gas, warm oil, or salt. For pressurized gas, a rapid quench rate to below 1000°F (538°C) is critical to obtain the desired properties. For oil, quench until black, about 900°F (482°C), then cool in still air to 150 -125°F (66-51°C). For salt maintained at 1000-1100°F (538-593°C), equalize, then cool in still air to 150 -125°F (66-51°C).
Tempering: Temper immediately after quenching. Typical tempering range is 1025-1050°F (552-566°C). Hold at temperature for 2 hours, then air cool to ambient temperature. Double tempering is required. For large cross sections, and especially for blanks from which tools will be cut by wire EDM, triple tempering is strongly recommended.
ANNEALING
Annealing must be performed after hot working and before re-hardening.
Heat at a rate not exceeding 400°F per hour (222°C per hour) to 1525-1550°F (829-843°C), and hold at temperature for 1 hour per inch (25.4 mm) of thickness, 2 hours minimum. Then cool slowly with the furnace at a rate not exceeding 50°F per hour (28°C per hour) to 1000°F (538°C). Continue cooling to ambient temperature in the furnace or in air. The resultant hardness should be 248 HBW or lower.
| Item | Dimension (mm) | Process | Delivery condition |
| Round Bar | DIA1.0 - 30 | Cold-drawing / Centerless grinding | Bright & Anneal |
| DIA20 - 80 | Peeling | Bright & Anneal | |
| DIA 13-180 | Hot Rolled | Black surface & Anneal | |
| DIA 70 - 400 | Hot Rolled | Black surface & Anneal | |
| Flat Bar | T 3.0-20 X W 20-100 | Hot Rolled | Black surface & Anneal |
| Block | T 20-200 X 300-800 | Hot Rolled & Hot Forged | Black surface /Machine & Anneal |
| Wire Rod | DIA 5.5 - 13 | Hot Rolled | Black surface & Anneal |
| Sheets | T1.0 - 2.5 | Cold Rolled | Black surface & Anneal |
| T 2.5 - 8.0 | Hot Rolled | Black surface & Anneal |